题目：Where is the maximal strength in face-center-cubic metals?
魏宇杰（研究员）
中国科学院力学研究所，非线性力学国家重点实验室（LNM）
(Email: yujie_wei（at）lnm.imech.ac.cn )
Abstract: In contrast to generally disordered grain boundaries (GBs), twin boundaries (TBs) are coherent and strong. Replacing general GBs by TBs - so that high strength and large deformability can be realized in polycrystals – has been a focus of metallurgical society for about one century. Recent success in manufacturing ultra-fine grained Cu with embedded nanotwins revealed that such nanotwinned metals are indeed strong; their yielding strength can be as high as 1 Gpa, which is 10 times stronger than their conventional counterparts. Intriguingly, such nanotwined Cu strengthens as TB spacing decreases to 15nm, then softens if TB spacing narrows further.
Here I will report our explanation about the softening mechanism in such nanotwinned metals. We found that nucleation of dislocations parallel to TBs governs the strength of such materials, resulting in their softening below a critical TB spacing. Large-scale molecular dynamics simulations and a kinetic theory of dislocation nucleation in nanotwinned metals show that there exists a transition in deformation mechanism, occurring at a critical TB spacing for which strength is maximized. The simulations indicate that the critical TB spacing for the onset of softening in nano-twinned copper and the maximum strength depend on the grain size: the smaller the grain size, the smaller the critical TB spacing, and the higher the maximum strength of the material.
464<span styletimes="" new="" roman';="" color:="" black;="" font-size:="" 10.5pt;="" font-weight:="" normal;="" mso-bidi-font-size:="" 12.0pt;="" mso-bidi-font-weight:="" bold;="" mso-ansi-language:="" en"="" lang="EN">, 877-880 (8 April 2010); <span styletimes="" new="" roman';="" color:="" black;="" font-size:="" 10.5pt;="" font-weight:="" normal;="" mso-bidi-font-size:="" 12.0pt;="" mso-fareast-font-family:="" 微软雅黑;="" mso-bidi-font-weight:="" bold;="" mso-ansi-language:="" en"="" lang="EN">Yujie Wei, Mat. Sci.
简介: 魏宇杰 研究员， 博士; 专业领域: 应用固体力学/材料力学;
学士，北京大学， 1992年9月—1997年7月； 硕士，中科院力学研究所 ，1997年9月—2000年7月；
博士，麻省理工学院 ， 2001年9月—2006年2月； 博士后，布朗大学，2006年3月—2008年12月；
助理教授，阿拉巴马大学（美国） 2009年1月—2010年1月； 研究员（百人计划），中科院力学研究所， 2010年2月—
主持人：曹国鑫 特聘研究员
时 间：12月3日（周五）下午1:45~3:15
地 点：力学楼434会议室
欢迎广大师生光临！